Zirconia Blocks
Better aesthetic performance than white zirconia.
Strictly follow up VITA® Classic Shade Guide.
Applicable to full arch and long bridge.
Bloomden® 3D Pro multilayer zirconia is unlike any other zirconia, it can exhibit a strength range from 800MPa to 1200MPa which can cover posteriors and anteriors for both crowns and bridges including implant restorations.
We provide exceptional color matching for VITA® 's full range of 16 shades, including BL2. Our quality is consistent across batches, and dental technicians in both Europe and the USA have confirmed our color accuracy.
Bloomden white zirconia's excellent masking effect. it is able to effectively cover up discolorations or dark spots, resulting in a more aesthetically pleasing appearance. This is especially important for patients who are self-conscious about their smile or want a restoration that looks as natural as possible.
Restorations are available with monolithic full contour crowns, bridges, veneers or full arch.
Veneer
Anterior crown
Posterior crown
Inlay
Full Crown Bridge
Impant crown
Implant full Arch
Full arch bridge
| Technical Specifications | |||
| UT Preshaded | ST-Plus Preshaded | ST Preshaded | |
| Zr02+HfO2+Y203 | ≥99% | ≥99% | ≥99% |
| Y203 | 9%-10% | 7.0%-7.8% | 4.5%-6.0% |
| AI203 | <0.5% | <0.15% | <0.5% |
| Density Before Sintering(g.cm-3) | 3.20±0.05 | 3.15±0.05 | 3.15±0.05 |
| Density After Sintering(g.cm-3) | 6.06±0.01 | 6.08±0.01 | 6.09±0.01 |
| CTE(25-500℃)(K-1) | 10.5±0.5 | 10.5±0.5 | 10.5±0.5 |
| Flexural Strength After Sintering(MPa) | >600 | >900 | >1100 |
| Aging Surface Monoclinic Phase Content | <15% | <15% | <15% |
| Light Transmittance | <49% | <46% | <43% |
| Chemical Solubility After Sintering(ug.cm-2) | <100 | <100 | <100 |
| Cytotoxicity | 0 Level | 0 Level | 0 Level |
| Radioactivity(Bq.g-1)) | <0.1 | <0.1 | <0.1 |
| Sintering Temperature(℃) | 1435-1470 | 1480-1530 | 1500-1530 |
| Systems | 98mm/95mm/92*75mm | ||
| Thickness | 12m/14mm/16mm/18mm/20mm/22mm/25mm | ||
| Shades | A1 A2 A3 A3.5 A4/B1 B2 B3 B4/C1 C2 C3 C4/D2 D3 D4 | ||
I have been using zirconia fast sintering technology for several months now, and I am thrilled with the results. The fast sintering process has significantly reduced the time it takes to produce high-quality zirconia restorations, allowing me to take on more work and increase my productivity. The strength and aesthetics of the restorations are just as good, if not better, than traditional sintering methods, and my patients have been extremely satisfied with the results. I appreciate the reduced energy consumption , which makes the process more environmentally friendly.
Overall, zirconia fast sintering technology has been a game-changer for my lab, and I would highly recommend it to any dental technician looking to improve their workflow and output quality.
Dr.Nathan Graves